Shalom

Transmission Range :

0.37 to 13.5 μm

Refractive Index :

2.20084 at 10 μm

Reflection Loss :

24.7% at 10 μm (2 surfaces)

Absorption Coefficient :

0.0006 cm-1 at 3.8 μm

Reststrahlen Peak :

30.5 μm

dn/dT :

+38.7 x 10-6 /°C at 3.39 μm

dn/dμ = 0 :

n/a

Density :

4.09 g/cc

Melting Point :

1827°C (See notes below)

Thermal Conductivity :

27.2 W m-1 K-1 at 298K

Thermal Expansion :

6.5 x 10-6 /°C at 273K

Hardness :

Knoop 160 with 50g indenter

Specific Heat Capacity :

515 J Kg-1 K-1

Dielectric Constant :

88

Youngs Modulus (E) :

74.5 GPa

Shear Modulus (G) :

n/a

Bulk Modulus (K) :

n/a

Elastic Coefficients :

Not Avalailable

Apparent Elastic Limit :

68.9 MPa (10,000 psi)

Poisson Ratio :

0.28

Solubility :

65 x 10-6 g/100g water

Molecular Weight :

97.43

Class/Structure :

HIP polycrystalline cubic, ZnS, F42m

µm

No

µm

No

µm

No

0.4047

2.54515

0.4358

2.48918

0.4678

2.44915

0.480 

2.43691

0.5086 

2.41279

0.5461 

2.38838

0.5876 

2.36789

0.6438

2.34731

0.6678 

2.34033

0.7065  

2.33073

0.780

2.31669

0.7948

2.31438

0.8521

2.30659

0.8943

2.30183

1.014

2.29165

1.1287

2.28485

1.5296  

2.27191

2.0581

2.26442

3.000 

2.25772

3.500

2.25498

4.000

2.25231

4.500

2.24955

5.000 

2.24661

8.000

2.22334

9.000

2.22334

10.00

2.20084

11.25

2.18317

12.00

2.17101

13.00

2.15252